Silico-manganese submerged arc furnace dephosphorization

 Silico-manganese alloy is a common compound deoxidizer, it is also a reducing agent. High-silicon-manganese-silicon alloy is used for external reduction dephosphorization. CaSi-CaF2-CaO is used as dephosphorization agent. Under the condition of extremely low oxygen potential, the combination of calcium in the dephosphorization agent and phosphorus in the alloy generates Ca3P2, which can make The phosphorus in the alloy is removed, and the alloying elements in the alloy are not lost.

The raw materials used in smelting high silicon-manganese silicon alloys are: manganese-rich slag, silica, coke, charcoal, and lime. The basic principle of reductive dephosphorization is to rely on the combination of calcium in the dephosphorizing agent and phosphorus in the alloy to generate Ca3P2 under the condition of extremely low oxygen potential, so that the phosphorus in the alloy can be removed.

Adopting process methods: inverted bag method, powder spraying method. Two hot metal ladle A and B are required. A hot metal is filled with high-silicon-manganese silicon alloy smelted in a submerged arc furnace, and a hot metal ladle is filled with a dephosphorization agent. Then hoist the ladle A to the ladle B, open the tap hole of the ladle A, and let the liquid high silicon manganese silicon alloy in the ladle A flow into the ladle B containing the dephosphorization agent. At this time, the dephosphorization agent The calcium in the alloy produces a fierce dephosphorization reaction with the phosphorus in the high-silico-manganese silicon alloy to remove the phosphorus in the alloy.

In the powder spraying method, the dephosphorization agent is loaded into a 0.25m powder spray tank, and the dephosphorization agent is sprayed into the high silicon manganese silicon alloy melt through the spray gun with argon gas as the carrier. The gas pressure is controlled at 0.2-0.3MPa, the fluidizing gas pressure is controlled at 0.5-0.8MPa, the powder spraying time is 2 to 3 minutes, and the amount of dephosphorization agent sprayed is the same as that of the inverted bag method. High silicon manganese silicon alloy is a reducing agent for smelting metal manganese.


Contact info:

Email: carbongraphiteproduct@gmail.com

whatsapp: +8614738833543


Henan Rongxin Carbon Group

　　Rongxing Group is China’s leading supplier dedicated to providing its customers with the quick quotes, superior quality products, competitive prices and fastest possible deliveries of carbon metallurgical materials and solutions.

　　Its main products are graphite electrode，electrode paste, calcined petroleum coke, and refractory. The range of product line covers carbon materials, graphite materials, refractory and water treatment materials. The annual production capacity of graphite electrode, electrode paste, calcined coke and refractory reaches 50,000 tons, 200,000 tons, 250,000 tons and 20,000 tons respectively. The company’s corporate headquarters is currently located in the Zhengzhou.

　　As an experienced supplier, we now offer everything from RP, HP to UHP graphite electrode and trapezodial, oval, cylinder electrode paste in the world. Our products meet and exceed the challenges of thousands of applications, and continue to be innovated.


Alibaba ：Graphite electrode

Alibaba ：Electrode paste

Location: XVH5+HQ 土耳其迪亚巴克尔省卡亚珀纳尔

Comments

Post a Comment

Popular posts from this blog

Study on impurities in high purity flake graphite

Image
 　　For the analysis of trace impurities in high-purity flake graphite, the sample is usually pre ashed or wet digested to remove carbon, the ash is dissolved with acid, and then the impurity content in the solution is determined. The ashing method does not need to use ultra pure acid to dissolve the ash, thus avoiding the risk of introducing the elements to be measured, so it is used more. It is also very difficult to detect the ash content of high-purity flake graphite, because the enriched ash needs to be burned at high temperature, and it is difficult to separate the ash from the sample boat at high temperature, which makes it impossible to accurately determine the composition and content of impurities. 　　The existing methods all take advantage of the characteristic that the platinum crucible does not react with acid, use the platinum crucible to burn the high-purity flake graphite to enrich ash, and then directly heat the sample in the crucible with acid to dissolve th
Read more

General technical index requirements for electrode paste

Image
 Electrode occupies an important position in submerged arc furnace. The working conditions of the electrode are bad, the current passing through is high, the temperature difference between the two ends is large, and the production is affected by the impact of mechanical, electrical and charge collapse... Mechanical strength, higher electrical resistivity, better thermal shock resistance, oxidation resistance and smaller thermal expansion coefficient. Generally speaking, the quality of electrode paste is controlled by the following five indicators: 1. Ash: Ash is the residue of electrode paste when it is burnt to constant weight at 850℃-870℃. It belongs to inorganic minerals. It has high ash resistivity, poor strength, high power consumption, and large electrode consumption. In the event of a hard breaking accident, the ash content is a very important indicator, and the lower the better. 2. Volatile matter: Volatile matter refers to the mass loss of electrode paste under the condition o
Read more

Performance characteristics of anthracite electrode paste

 Anthracite is the main raw material of electrode paste. The performance of anthracite is related to the performance of electrode paste. Therefore, it is necessary to understand and discuss the performance of anthracite to ensure the quality of electrode paste. Anthracite coal in China is mainly distributed in Shanxi, Ningxia and Guizhou. Shanxi is the origin of anthracite, which is mainly produced in Yangquan and Jincheng. Anthracite is an indispensable raw material for carbon industry. It is mainly used in semi graphite cathode carbon block, electric furnace carbon block, blast furnace carbon block, carbon electrode and various pastes. Studying and discussing various properties of anthracite is very beneficial to improve the quality of carbon products.
Read more