CGM Online

 Electrode paste manufacturing includes such production processes as medium crushing and screening, grinding, batching, kneading and molding cooling. ① Medium crushing screening The project is equipped with a medium crushing and screening system for calcined anthracite. The calcined anthracite is fed by electromagnetic vibrating feeder, and then sent to a double-layer horizontal vibrating screen and a single-layer horizontal vibrating screen by belt conveyor and bucket elevator. After screening, the materials with particle size greater than 10mm are returned to the intermediate bin, and then fed by electromagnetic vibrating feeder to the double roller crusher. Re sieving after medium crushing. 10-6mm and 6-3mm grain size materials can be directly into the corresponding batching bin, or can be returned to the double roller crusher to be finely crushed to less than 3mm, which is convenient for flexible production adjustment. There are 3 kinds of particle size materials, i.e. 10-

 When the sintering temperature of the electrode paste is between 300 and 800 degrees, because the volatile matter of the coal tar pitch has been discharged, the remaining coal tar pitch has been carbonized to form a network, and it is fused with various electrode paste raw materials, and the mechanical strength reaches the standard value. Our Rongxin Carbon technicians have calculated that the compressive strength of the electrode paste at this time is 17-33 MPa, the flexural strength is 7--17 MPa, and the tensile strength is 4--8 MPa. After the electrode below the copper tile of the submerged electric furnace enters the smelting process, the temperature of the electrode will rise further due to the further increase in the temperature of the raw material, and the mechanical strength will increase with the rise in temperature. The temperature of other materials rises to 1500 degrees. When the mechanical strength drops sharply, such as heat-resistant alloys, the mechanical strength of c

 1. Calcining. Both petroleum coke and pitch coke need to be calcined, and the calcining temperature should reach 1350. C, to fully remove the volatile matter contained in the carbonaceous raw materials, and improve the true density, mechanical strength, and conductivity of the coke. 2. Crushing, screening and batching. The calcined carbonaceous raw material is crushed and sieved into aggregate particles of specified size, part of the coke is ground into fine powder, and then weighed according to the formula to form a dry mixture of various particles. 3. Kneading. Under the heating state, the quantitative dry mixture of various particles and the quantitative binder are stirred and mixed and kneaded to form a plastic paste. 4. Forming. Under the action of external pressure or high-frequency vibration, the paste is pressed into a green electrode with a certain shape and higher density. 5. Roasting. Put the green electrode in a special roasting furnace, and use metallurgical coke powder t

 The graphite material is mainly composed of polycrystalline graphite. Graphite is a multi-layer laminated crystal with a hexagonal planar network structure between carbon atoms. Although graphite material is an inorganic non-metallic material, it has good thermal and electrical conductivity, and at the same time has a thermal expansion coefficient far lower than that of metal, a high melting point and chemical stability, which makes graphite materials very useful in industrial applications. High value. Graphite materials are chemically inert in non-oxidizing media and have good corrosion resistance. Except for strong acids and strong oxidizing media, graphite materials are not corroded by other acids, alkalis, and salts, and hardly react with organic compounds. . Graphite material is also a kind of high temperature resistant material. Graphite will not melt under high temperature, but at 3350 under normal pressure. C began to slowly sublimate into gas. The strength of general material