Measures to prevent electrode paste from breaking

 The measures to prevent electrode soft break during the use of electrode paste can be divided into the following points:

1. Strictly control and master the length of the working end of the electrode, reasonably control the pressing time, so that the pressing speed is compatible with the sintering speed. When the material surface is processed every 24 hours, Observe the baking condition of the electrode so as to control the hardness and softness of the electrode (if it is found that the surface of the laid down electrode is gray white, dark but not red or slightly red, it indicates that the electrode is well roasted; if the surface of the laid down electrode is red, it indicates that the electrode has been burnt; if the surface is black, it indicates that the electrode is not baked enough.

You can also use round steel to poke the electrode. If it is hard, it can bounce back to indicate that the electrode has been burnt; if it is elastic, it indicates that it is normal; if it is soft, it indicates that the electrode is not burnt.) If it is found that the electrode is black or emits yellow smoke, it will immediately judge that the electrode is soft, and the heating element should be turned on for low-level roasting and the pressure release time should be extended.

2. Strictly control the quality of the electrode paste to ensure that the volatile, ash and particle size are appropriate. 3. Strictly control the welding quality of the electrode barrel (no holes and sand holes).

3. After power off, the load shall not increase too fast. Observe the change of electrode quality, increase the load appropriately according to the baking quality of the electrode. If the electrode quality is found to be soft, reduce the load (power off) in time, and strictly control the electrode pressure release time (not exceeding the * pressure release time of the gear) and the pressure release length (strictly control the electrode pressure release exceeding 20mm).

4. Add the electrode paste on time and in quantity, and maintain the specified paste column height. If the operator finds that the paste column has not changed for a long time, he shall organize personnel to smash the paste and compact the overhead paste column. With good electrode quality.

5. Strictly control the moisture content of raw materials so as not to burn the insulation.

6. Regularly build the electrode insulation device and sealing device to keep the electrode in good working condition.

Comments

Post a Comment

Popular posts from this blog

Study on impurities in high purity flake graphite

Image
 　　For the analysis of trace impurities in high-purity flake graphite, the sample is usually pre ashed or wet digested to remove carbon, the ash is dissolved with acid, and then the impurity content in the solution is determined. The ashing method does not need to use ultra pure acid to dissolve the ash, thus avoiding the risk of introducing the elements to be measured, so it is used more. It is also very difficult to detect the ash content of high-purity flake graphite, because the enriched ash needs to be burned at high temperature, and it is difficult to separate the ash from the sample boat at high temperature, which makes it impossible to accurately determine the composition and content of impurities. 　　The existing methods all take advantage of the characteristic that the platinum crucible does not react with acid, use the platinum crucible to burn the high-purity flake graphite to enrich ash, and then directly heat the sample in the crucible with acid to dissolve th
Read more

General technical index requirements for electrode paste

Image
 Electrode occupies an important position in submerged arc furnace. The working conditions of the electrode are bad, the current passing through is high, the temperature difference between the two ends is large, and the production is affected by the impact of mechanical, electrical and charge collapse... Mechanical strength, higher electrical resistivity, better thermal shock resistance, oxidation resistance and smaller thermal expansion coefficient. Generally speaking, the quality of electrode paste is controlled by the following five indicators: 1. Ash: Ash is the residue of electrode paste when it is burnt to constant weight at 850℃-870℃. It belongs to inorganic minerals. It has high ash resistivity, poor strength, high power consumption, and large electrode consumption. In the event of a hard breaking accident, the ash content is a very important indicator, and the lower the better. 2. Volatile matter: Volatile matter refers to the mass loss of electrode paste under the condition o
Read more

Performance characteristics of anthracite electrode paste

 Anthracite is the main raw material of electrode paste. The performance of anthracite is related to the performance of electrode paste. Therefore, it is necessary to understand and discuss the performance of anthracite to ensure the quality of electrode paste. Anthracite coal in China is mainly distributed in Shanxi, Ningxia and Guizhou. Shanxi is the origin of anthracite, which is mainly produced in Yangquan and Jincheng. Anthracite is an indispensable raw material for carbon industry. It is mainly used in semi graphite cathode carbon block, electric furnace carbon block, blast furnace carbon block, carbon electrode and various pastes. Studying and discussing various properties of anthracite is very beneficial to improve the quality of carbon products.
Read more