16.5Mva uses closed paste submerged arc furnace oven process

 Firewood

The main purpose of wood baking is to dry the moisture in the furnace and to initially bake the electrodes. Compared with coke and electric baking, wood baking has a larger baking area but a lower temperature, so the time is longer, generally lasting three to five days. Before the firewood is baked, the electrode paste is cushioned with refractory bricks to prevent adhesion. In the early stage of wood baking, the flame height does not exceed the furnace mouth. In the later stage, the electrode is baked with a high fire to make the wood burn evenly and violently.

Burnt

Before the coke is baked, a circle of flower wall with clay bricks is used to hold the coke around the electrode, and the height is lower than that of the furnace mouth. A layer of 100mm thick coke powder is placed on the bottom of the furnace to prevent oxidation at the bottom of the furnace. During the coking process, always observe the melting of the electrode paste, the height of the electrode paste, the change in the shape of the electrode shell, and the overflow of volatiles. During the baking process, the height of the electrode paste should always be kept consistent, and the amount of cooling water should be adjusted to prevent incomplete melting of the electrode paste. The coking time is about 30 hours.

Electric bake

Check various equipment before electric baking, and quickly clean the burnt ashes and clay bricks. Lift the electrode and spread 200mm thick coke on the bottom of the furnace, and lower the electrode to start the arc. During electric baking, the current should be gradually increased to 50%-60% of the smelting current being produced. There will be a power outage every two hours for 10-15 minutes in the early stage, and a power outage for 10-15 minutes every 3-4 hours in the later stage. After each power outage, the operation of the waterway and equipment should be carefully checked. After the end, the coke of the oven is quickly cleaned, and a small amount of coke remains around the electrode, then the electrode is put down, and some new coke is added to start the arc, and the material is fed after the arc is stabilized.

Contact info:

Email: carbongraphiteproduct@gmail.com

whatsapp: +8614738833543


Henan Rongxin Carbon Group

　　Rongxing Group is China’s leading supplier dedicated to providing its customers with the quick quotes, superior quality products, competitive prices and fastest possible deliveries of carbon metallurgical materials and solutions.

　　Its main products are graphite electrode，electrode paste, calcined petroleum coke, and refractory. The range of product line covers carbon materials, graphite materials, refractory and water treatment materials. The annual production capacity of graphite electrode, electrode paste, calcined coke and refractory reaches 50,000 tons, 200,000 tons, 250,000 tons and 20,000 tons respectively. The company’s corporate headquarters is currently located in the Zhengzhou.

　　As an experienced supplier, we now offer everything from RP, HP to UHP graphite electrode and trapezodial, oval, cylinder electrode paste in the world. Our products meet and exceed the challenges of thousands of applications, and continue to be innovated.


Alibaba ：Graphite electrode

Alibaba ：Electrode paste

Comments

Post a Comment

Popular posts from this blog

Study on impurities in high purity flake graphite

Image
 　　For the analysis of trace impurities in high-purity flake graphite, the sample is usually pre ashed or wet digested to remove carbon, the ash is dissolved with acid, and then the impurity content in the solution is determined. The ashing method does not need to use ultra pure acid to dissolve the ash, thus avoiding the risk of introducing the elements to be measured, so it is used more. It is also very difficult to detect the ash content of high-purity flake graphite, because the enriched ash needs to be burned at high temperature, and it is difficult to separate the ash from the sample boat at high temperature, which makes it impossible to accurately determine the composition and content of impurities. 　　The existing methods all take advantage of the characteristic that the platinum crucible does not react with acid, use the platinum crucible to burn the high-purity flake graphite to enrich ash, and then directly heat the sample in the crucible with acid to dissolve th
Read more

General technical index requirements for electrode paste

Image
 Electrode occupies an important position in submerged arc furnace. The working conditions of the electrode are bad, the current passing through is high, the temperature difference between the two ends is large, and the production is affected by the impact of mechanical, electrical and charge collapse... Mechanical strength, higher electrical resistivity, better thermal shock resistance, oxidation resistance and smaller thermal expansion coefficient. Generally speaking, the quality of electrode paste is controlled by the following five indicators: 1. Ash: Ash is the residue of electrode paste when it is burnt to constant weight at 850℃-870℃. It belongs to inorganic minerals. It has high ash resistivity, poor strength, high power consumption, and large electrode consumption. In the event of a hard breaking accident, the ash content is a very important indicator, and the lower the better. 2. Volatile matter: Volatile matter refers to the mass loss of electrode paste under the condition o
Read more

Performance characteristics of anthracite electrode paste

 Anthracite is the main raw material of electrode paste. The performance of anthracite is related to the performance of electrode paste. Therefore, it is necessary to understand and discuss the performance of anthracite to ensure the quality of electrode paste. Anthracite coal in China is mainly distributed in Shanxi, Ningxia and Guizhou. Shanxi is the origin of anthracite, which is mainly produced in Yangquan and Jincheng. Anthracite is an indispensable raw material for carbon industry. It is mainly used in semi graphite cathode carbon block, electric furnace carbon block, blast furnace carbon block, carbon electrode and various pastes. Studying and discussing various properties of anthracite is very beneficial to improve the quality of carbon products.
Read more