Furnace building for smelting Al-Si-Fe alloy in submerged arc furnace

Build a furnace

The main aluminum refractory material is high-alumina brick masonry. Three layers of graphite carbon bricks are built on the bottom of the furnace, and one layer of graphite carbon bricks are built on the walls of the furnace. A layer of electrode paste is knotted at the bottom of the furnace before starting the furnace, with an average thickness of 200mm.

Raw material preparation

Bauxite Content: AL2O3 55%-90% SIO2 20%-30%. Granularity: 30-120mm Rinse clean

Bituminous coal

Compared with other alloys in the smelting of silicon-aluminum-iron alloy submerged arc furnace electrode paste smelting, the application of the original agent is the most unique. Among the reducing agents used, bituminous coal accounts for more than 80%. Composition: 15%-25% volatile, less than 20% ash, less than 55% fixed carbon, good slagging performance.

Silica

In fact, the normal smelting of silicon-aluminum-ferroalloy does not have high requirements for silica. We have used it from 90% to 99% of the SiO2 content, and even used over-mature silica, which does not have a great impact on the smelting. Except for special circumstances, generally more than 95% of silica can be used. However, there are still strict requirements when opening the furnace: SiO2 is greater than 98%, good anti-explosion, cleaned, and the particle size is below 100mm.

Iron bauxite

This kind of raw material is indispensable in our electrode paste submerged arc furnace smelting test, and it has a certain catalytic effect on the reduction of aluminum during the entire smelting process.

Ingredients

The ingredients for furnace smelting should take into account factors such as low furnace temperature. Ferrosilicon can be used to open the furnace and then to smelt ferrosilicon and aluminum. However, we all use the direct electrode paste submerged arc furnace to smelt ferrosilicon and aluminum. The raw material batch for the furnace is based on the 25% aluminum content and 35% silicon content of the baked product. Carbon-rich operation is required when the furnace is opened. According to different raw materials, accurate batches cannot be given here.

Contact info:

Email: carbongraphiteproduct@gmail.com

whatsapp: +8614738833543


Henan Rongxin Carbon Group

　　Rongxing Group is China’s leading supplier dedicated to providing its customers with the quick quotes, superior quality products, competitive prices and fastest possible deliveries of carbon metallurgical materials and solutions.

　　Its main products are graphite electrode，electrode paste, calcined petroleum coke, and refractory. The range of product line covers carbon materials, graphite materials, refractory and water treatment materials. The annual production capacity of graphite electrode, electrode paste, calcined coke and refractory reaches 50,000 tons, 200,000 tons, 250,000 tons and 20,000 tons respectively. The company’s corporate headquarters is currently located in the Zhengzhou.

　　As an experienced supplier, we now offer everything from RP, HP to UHP graphite electrode and trapezodial, oval, cylinder electrode paste in the world. Our products meet and exceed the challenges of thousands of applications, and continue to be innovated.


Alibaba ：Graphite electrode

Alibaba ：Electrode paste

Comments

Post a Comment

Popular posts from this blog

Study on impurities in high purity flake graphite

Image
 　　For the analysis of trace impurities in high-purity flake graphite, the sample is usually pre ashed or wet digested to remove carbon, the ash is dissolved with acid, and then the impurity content in the solution is determined. The ashing method does not need to use ultra pure acid to dissolve the ash, thus avoiding the risk of introducing the elements to be measured, so it is used more. It is also very difficult to detect the ash content of high-purity flake graphite, because the enriched ash needs to be burned at high temperature, and it is difficult to separate the ash from the sample boat at high temperature, which makes it impossible to accurately determine the composition and content of impurities. 　　The existing methods all take advantage of the characteristic that the platinum crucible does not react with acid, use the platinum crucible to burn the high-purity flake graphite to enrich ash, and then directly heat the sample in the crucible with acid to dissolve th
Read more

General technical index requirements for electrode paste

Image
 Electrode occupies an important position in submerged arc furnace. The working conditions of the electrode are bad, the current passing through is high, the temperature difference between the two ends is large, and the production is affected by the impact of mechanical, electrical and charge collapse... Mechanical strength, higher electrical resistivity, better thermal shock resistance, oxidation resistance and smaller thermal expansion coefficient. Generally speaking, the quality of electrode paste is controlled by the following five indicators: 1. Ash: Ash is the residue of electrode paste when it is burnt to constant weight at 850℃-870℃. It belongs to inorganic minerals. It has high ash resistivity, poor strength, high power consumption, and large electrode consumption. In the event of a hard breaking accident, the ash content is a very important indicator, and the lower the better. 2. Volatile matter: Volatile matter refers to the mass loss of electrode paste under the condition o
Read more

Performance characteristics of anthracite electrode paste

 Anthracite is the main raw material of electrode paste. The performance of anthracite is related to the performance of electrode paste. Therefore, it is necessary to understand and discuss the performance of anthracite to ensure the quality of electrode paste. Anthracite coal in China is mainly distributed in Shanxi, Ningxia and Guizhou. Shanxi is the origin of anthracite, which is mainly produced in Yangquan and Jincheng. Anthracite is an indispensable raw material for carbon industry. It is mainly used in semi graphite cathode carbon block, electric furnace carbon block, blast furnace carbon block, carbon electrode and various pastes. Studying and discussing various properties of anthracite is very beneficial to improve the quality of carbon products.
Read more