Characteristic effect of carburizing agent

　　The characteristics of carburizing agent are that pure carbon containing graphitization material is selected to reduce excessive impurities in pig iron, and proper selection of carburizing agent can reduce the production cost of castings. There are many kinds of raw materials and production processes of carburizing agent. It is not said in the market that graphite powder is pressed and formed. This production method needs to add too much binder to form, and the carbon content generally cannot meet the requirements of high-quality carburizing agent. The pressed graphite powder is a solid block without a porous structure, so the absorption rate and absorption rate are not as good as those of calcined and calcined carburizers.

　　The use of carburizing agent in casting can greatly increase the amount of scrap steel, reduce the amount of pig iron or not use pig iron. At present, most of the carburizers are suitable for electric furnace smelting, and a small number of carburizers with particularly fast absorption rate are used for cupola. The amount of carburizing agent shall be determined according to the proportion and carbon content of other raw materials. For different types of cast iron, different types of carburizing agents can be selected according to needs. It is necessary to avoid feeding molten iron in large quantities to prevent excessive oxidation, which leads to poor carburizing effect and insufficient carbon content of castings.

　　High quality carburizers generally refer to graphitized carburizers. Under high temperature conditions, the arrangement of carbon atoms is in the microscopic form of graphite, so it is called graphitization. Graphitization can reduce the content of impurities in the carburizing agent, increase the carbon content of the carburizing agent and reduce the sulfur content.

Comments

Post a Comment

Popular posts from this blog

Study on impurities in high purity flake graphite

Image
 　　For the analysis of trace impurities in high-purity flake graphite, the sample is usually pre ashed or wet digested to remove carbon, the ash is dissolved with acid, and then the impurity content in the solution is determined. The ashing method does not need to use ultra pure acid to dissolve the ash, thus avoiding the risk of introducing the elements to be measured, so it is used more. It is also very difficult to detect the ash content of high-purity flake graphite, because the enriched ash needs to be burned at high temperature, and it is difficult to separate the ash from the sample boat at high temperature, which makes it impossible to accurately determine the composition and content of impurities. 　　The existing methods all take advantage of the characteristic that the platinum crucible does not react with acid, use the platinum crucible to burn the high-purity flake graphite to enrich ash, and then directly heat the sample in the crucible with acid to dissolve th
Read more

General technical index requirements for electrode paste

Image
 Electrode occupies an important position in submerged arc furnace. The working conditions of the electrode are bad, the current passing through is high, the temperature difference between the two ends is large, and the production is affected by the impact of mechanical, electrical and charge collapse... Mechanical strength, higher electrical resistivity, better thermal shock resistance, oxidation resistance and smaller thermal expansion coefficient. Generally speaking, the quality of electrode paste is controlled by the following five indicators: 1. Ash: Ash is the residue of electrode paste when it is burnt to constant weight at 850℃-870℃. It belongs to inorganic minerals. It has high ash resistivity, poor strength, high power consumption, and large electrode consumption. In the event of a hard breaking accident, the ash content is a very important indicator, and the lower the better. 2. Volatile matter: Volatile matter refers to the mass loss of electrode paste under the condition o
Read more

Performance characteristics of anthracite electrode paste

 Anthracite is the main raw material of electrode paste. The performance of anthracite is related to the performance of electrode paste. Therefore, it is necessary to understand and discuss the performance of anthracite to ensure the quality of electrode paste. Anthracite coal in China is mainly distributed in Shanxi, Ningxia and Guizhou. Shanxi is the origin of anthracite, which is mainly produced in Yangquan and Jincheng. Anthracite is an indispensable raw material for carbon industry. It is mainly used in semi graphite cathode carbon block, electric furnace carbon block, blast furnace carbon block, carbon electrode and various pastes. Studying and discussing various properties of anthracite is very beneficial to improve the quality of carbon products.
Read more